Radici Compounds PC10L V0

聚碳酸酯

Radici Plastics USA, Inc.

Technical Data

 

产品说明

 

PC10L VO is a polycarbonate compound with a viscosity suitable for general purpose injection molding applications, flame retarded to meet the V-O requirements of Underwriters' Laboratories Bulletin 94 at section thicknesses of 1/16 inch or greater.

 

Polycarbonate is an engineering thermoplastic widely recognized for outstanding toughness, excellent strength, rigidity and creep resistance, electrical insulation and dimensional stability. Mold shrinkage is low and almost isotropic; this offers benefits in dimensional stability and reduced warpage, and permits the production of complex shape parts to very close dimensional tolerances.

 

Polycarbonate must be dried prior to processing to fully realize the mechanical properties of the material and the excellent surface appearance typical of parts molded in polycarbonate resins.

 

总体

 

材料状态 • 已商用：当前有效

搜索 UL 黄卡 •  Radici Plastics USA, Inc.

供货地区 • 北美洲

添加剂 • 润滑剂 • 阻燃

• 尺寸稳定性良好 • 绝缘 • 收缩性低

• 刚性，高 • 抗弯曲

性能特点 • 外观良好

• 高强度 • 良好的抗蠕变性

• 阻燃性能

• 经润滑 • 韧性良好

外观 • 可用颜色 • 自然色

形式 • 颗粒料

加工方法 • 注射成型

 

物理性能 额定值单位制 测试方法

比重 1.21g/cm³ ASTM D792

收缩率 - 流动 (3.18 mm) 0.50 到 0.70% ASTM D955

吸水率 (24 hr) 0.15% ASTM D570

机械性能 额定值单位制 测试方法

抗张强度 2 (屈服, 23°C, 3.18 mm) 62.1MPa ASTM D638

伸长率 2 (断裂, 23°C, 3.18 mm) 80% ASTM D638

弯曲模量 (23°C) 2340MPa ASTM D790

弯曲强度 (23°C) 93.1MPa ASTM D790

冲击性能 额定值单位制 测试方法

悬壁梁缺口冲击强度 (23°C, 3.18 mm) 690J/m ASTM D256

硬度 额定值单位制 测试方法

洛氏硬度 (M 计秤) 70 ASTM D785

热性能 额定值单位制 测试方法

热变形温度 (1.8 MPa, 未退火) 128°C ASTM D648

维卡软化温度 154°C ASTM D1525

可燃性 额定值单位制 测试方法

UL 阻燃等级 (1.59 mm, NC) V-0 UL 94

补充信息

Elongation at Break, ASTM D638, Type I, 73°F, 0.125": 70-90 %

Izod Impact Strength, ASTM D256, Notched, 73°F: 12-14 ft-lbs/in

注射 额定值单位制

干燥温度 121°C

干燥时间 4.0hr

建议的最大水分含量 0.020%

螺筒后部温度 282°C

螺筒中部温度 288°C

螺筒前部温度 293°C

加工（熔体）温度 293°C

模具温度 82.2 到 93.3°C

 

 

Radici Compounds PC10L V0

聚碳酸酯

Radici Plastics USA, Inc.

注射 额定值单位制

背压 0.345 到 0.689MPa

螺杆转速 40 到 80rpm

 

 

 

 

 