EMERGE™ PC 4903
Advanced Resin

Styron LLC  
    
 Technical Data   
    

产品说明

EMERGE PC 4903 is a 30% glass fiber reinforced high flow ignition resistant polycarbonate resin. This resin does not contain bromine and chlorine flame retardants. EMERGE PC 4903 is designed with superior processability for use in structural parts of printers, scanners, copiers as well as internal parts for ITE applications.

Applications:
• Structural parts of printers, scanners, and copiers

• Internal parts of ITE machines

总体

材料状态 • 已商用：当前有效 
资料 1 •  Technical Datasheet

UL Yellow Card 2 •  E206114-509989

Search for UL Yellow Card •  Styron LLC

 •  EMERGE™

  
供货地区 • 亚太地区 
填料/增强材料 • 玻璃纤维增强材料, 30% 填料按重量 
添加剂 • 阻燃 
形式 • 颗粒料 
加工方法 • 注射成型 

物理性能  额定值单位制 测试方法
熔流率 (300°C/1.2 kg)  12g/10 min ASTM D1238
收缩率 - 流动 0.20 到 0.40% ASTM D955
机械性能  额定值单位制 测试方法
抗张强度 (屈服, 3.20 mm, 注塑)  116MPa ASTM D638
弯曲模量 (3.20 mm, 注塑)  8400MPa ASTM D790
弯曲强度 (3.20 mm, 注塑)  172MPa ASTM D790
冲击性能  额定值单位制 测试方法
悬壁梁缺口冲击强度 (23°C, 3.20 mm, 注塑)  130J/m ASTM D256
热性能  额定值单位制 测试方法
热变形温度 (1.8 MPa, 未退火)  110°C ASTM D648
可燃性  额定值单位制 测试方法
UL 阻燃等级 4 (1.60 mm)  V-0 UL 94
   
注射  额定值单位制 
干燥温度  120°C 
干燥时间 3.0 到 4.0hr 
螺筒后部温度 250 到 260°C 
螺筒中部温度 260 到 270°C 
螺筒前部温度 260 到 280°C 
射嘴温度 270 到 290°C 
模具温度 60.0 到 100°C